Slurry mixing involves combining active materials, conductive additives, binders, and solvents to create a homogeneous electrode slurry mixture[1] . This slurry is then coated onto a current collector to form the electrode. Proper slurry mixing ensures optimal performance, consistency, and longevity of the batteries.
A video demonstrating the consistency of lithium-ion battery electrode slurry consistency after different stages of mixing
Preparation
Weighing: This step involves precisely measuring each component of the slurry to match the desired electrode composition. Accurate weighing ensures the correct ratio of active materials, conductive additives, binders, and solvents, which is crucial for the performance and consistency of the final battery.
Pre-mixing: Before adding any liquids, the dry powders (active materials and conductive additives) are pre-mixed. This helps in achieving a uniform distribution of particles, preventing segregation, and ensuring that all subsequent mixing steps result in a homogenous slurry.
Dispersion
Add Solvent: The solvent is added gradually to the pre-mixed dry powders while stirring at a low speed. This careful addition prevents the formation of agglomerates, which are clumps of particles that can affect the uniformity and performance of the slurry.
High-speed Mixing: Using high-shear mixers or ball mills, the slurry is mixed at high speeds to break down any remaining agglomerates. This step, which can take several hours, ensures that the particles are evenly distributed throughout the mixture, resulting in a smooth and consistent slurry.
Binder Addition
Slow Addition: The binder is added slowly to the slurry while continuously mixing. Adding the binder gradually helps prevent clumping, ensuring that the binder is evenly distributed throughout the slurry.
High-shear Mixing: After adding the binder, high-shear mixing continues to ensure that the binder is fully dissolved and homogeneously mixed. This step is critical for the mechanical stability and adhesion properties of the final electrode.
Homogenization
Vacuum Deaeration: Air bubbles trapped in the slurry can cause defects in the coated electrodes. Vacuum deaeration removes these bubbles by applying a vacuum to the slurry, ensuring a defect-free coating process.
Final Mixing: The slurry undergoes a final mixing phase at a moderate speed. This ensures that the mixture is completely homogeneous, with all components evenly distributed, ready for the coating process on the current collector.
Equipment
Mixers
an image of a pilot-scale battery electrode slurry mixer
Planetary Mixers: Ideal for small-scale or laboratory use, providing thorough mixing with minimal shear.
High-shear Mixers: Suitable for large-scale production, offering efficient particle dispersion and homogenization.
Ball Mills: Used for breaking down agglomerates and achieving fine particle distribution.
Dispersers
Ultrasonic Dispersers: Utilize ultrasonic waves to break up particle agglomerates.
Bead Mills: Employ grinding beads to achieve fine dispersion of particles.
Process Parameters
Temperature: Maintain a controlled temperature (typically 25-40°C) to ensure binder solubility and prevent solvent evaporation.
Mixing Speed: Optimize mixing speed based on the slurry viscosity and desired particle size distribution. High speeds enhance dispersion but may cause excessive heating.
Mixing Time: Ensure adequate mixing time to achieve homogeneity without over-mixing, which can cause degradation of materials.
Quality Control
Viscosity Measurement
Regularly measure slurry viscosity using viscometers to ensure consistency. Target viscosity varies depending on the electrode type but is generally within the range of 500-5000 cP.
Particle Size Analysis
A grindometer is used to assess the particle size distribution in a battery slurry, which is critical for ensuring uniformity and optimal performance. By measuring how finely the active materials and conductive agents are dispersed, the grindometer helps in determining the slurry’s consistency, which directly impacts the battery's electrochemical properties and cycle life.
Cause: Insufficient mixing or inadequate dispersing agent.
Solution: Increase mixing time or speed, or add more dispersing agent.
Viscosity Fluctuations
Cause: Inconsistent binder or solvent addition.
Solution: Ensure precise and controlled addition of components.
Poor Adhesion
Cause: Incomplete binder dissolution or inadequate mixing.
Solution: Extend mixing time and ensure thorough binder integration.
Proper slurry mixing is essential for high-performance battery electrodes. By following these guidelines and continuously monitoring process parameters, manufacturers can achieve consistent and reliable slurry formulations.